The structure and optical characteristics of thin (∼30 nm) wurtzite AlInN films grown pseudomorphic on free-standing, c-plane GaN substrates are presented. The Al1−xInxN layers are grown by metalorganic chemical vapor deposition, resulting in films with varying In content from x = 0.142 to 0.225. They are measured using atomic force microscopy, x-ray diffraction, reciprocal space mapping, and spectroscopic ellipsometry (SE). The pseudomorphic AlInN layers provide a set where optical properties can be determined without additional variability caused by lattice relaxation, a crucial need for designing devices. They have smooth surfaces (rms < 0.29 nm) with minimum pit areas when the In content is near lattice-matched to GaN. As expected, SE shows that the refractive index increases and the bandgap energy decreases with increased In-content. Plots of bandgap energy vs In content are fitted with a single bowing parameter of 3.19 eV when using bandgap energies for AlN and InN pseudomorphic to GaN, which is lower than previous measurements and closer to theoretical predictions. 

Near-infrared electroluminescence of InGaN quantum dots (QDs) formed by controlled growth on photoelectrochemical (PEC) etched QD templates is demonstrated. The QD template consists of PEC InGaN QDs with high density and controlled sizes, an AlGaN capping layer to protect the QDs, and a GaN barrier layer to planarize the surface. Scanning transmission electron microscopy (STEM) of Stranski–Krastanov (SK) growth on the QD template shows high-In-content InGaN QDs that align vertically to the PEC QDs due to localized strain. A high-Al-content${\mathrm{Al}}_{0.9}{\mathrm{Ga}}_{0.1}\mathrm{N}$capping layer prevents the collapse of the SK QDs due to intermixing or decomposition during higher temperature GaN growth as verified by STEM. Growth of low-temperature (830°C) p-type layers is used to complete the p-n junction and further ensure QD integrity. Finally, electroluminescence shows a significant wavelength shift (800 nm to 500 nm), caused by the SK QDs’ tall height, high In content, and strong polarization-induced electric fields.